COLD FORMING MATERIALS

X5 CrNiMo 17 -12-2 CHQ丝

MATERIALSENGINEERINGCREATION GROUP

产品中心 / X5 CrNiMo 17 -12-2 CHQ丝

X5 CrNiMo 17 -12-2 CHQ丝

直径: 0.40-46mm

拉伸强度: 参考技术信息

Product Detail Technical Information Inspection Packaging

上海创造集团是中国专注于冷轧优质钢丝的标杆企业，整个管理团队拥有20年的行业经验。我们与多家汽车行业一级供应商建立了良好的关系，所有钢丝均来自品牌钢厂。所有订单均100%可追溯。

Specification

+AT或+AT+PE

+AT+C

+AT+C+AT

+AT+C+AT+LC

Specification

- : 连续且平滑

- : 无接缝、重叠、坑坑、划痕和拉拔划痕

- : 不应有锈迹

Specification

- : 汽车产业

- : 建筑业

- : 机械行业

- : 其他行业

Case Study

Products & Service

盘条

酸洗与磷化

冷拉拔

球化退火

检查

成品

1.交货条款组合

表D.1 -交货时热处理条件、产品形式和适用要求的组合

Heat-treat- ment con- dition at delivery	Symbol	Product form a			Steel a			Applicable requirements
Heat-treat- ment con- dition at delivery	Symbol	Wire rod	Bar	Wire	Ferri- tic	Marten- sitic	Austenit- ic and austenit- ic- ferritic	Applicable requirements
Solution annealed or solution annealed +peeled	+AT or AT+PE	X	X	X	—	一	X	Chemical compo- sition as specified inTable D.2	Mechani- cal prop- erties as speci- fied in Tables D.3, D.4 and D.6	Supple- mentary or special re- quirements as specified in Annex Eb
Solution annealed +cold drawn	+AT+C	一	X	X	—	—	X
Solution an- nealed +cold drawn + solution an- nealed	+AT+C +AT		X	X			X
Solution an- nealed +cold drawn+solu- tion annealed + skin passed	+AT+C +AT+ LC		X	X			X
Soft annealed or soft annealed + peeled	+A or +A+PE	X	X	X	X	X	—
Soft annealed + skin passed	+A+LC	—	X	X	X	X	—
Soft annealed + cold drawn + soft annealed	+A+C +A		X	X	X	X
Soft annealed + cold drawn+ soft annealed + skin passed	+A+C +A+LC	—	X	X	X	X	—
Others	Other delivery conditions may be agreed at the time of enquiry and order.
a X=applicable,-=not applicable. b If agreed at the time of the enquiry and order

2.化学成分

表D.2-不锈钢牌号的化学成分（适用于铸件分析）

Designation		% mass fraction a
Steel name	ISO steel number	C	Si		Mn		P		S		Cr		Ni		Mo		N		Cu		Others
Austenitic steels
X10CrNi18-8	4310-301-00-1	0,05 to 0,15		2,00		2,00		0,045		0,015		16,0 to 19,0		6,0 to 9,5		0,80		0,10		1,00		—
X2CrNi18-9	4307-304- 03-1	0,030		1,00		2,00		0,045		0,030		17,5 to 19,5		8,0 to 10,0		一		0,10		1,00		—
X6CrNiCu18-9-2	4567-304- 98-X	0,08		1,00		2,00		0,045		0,030		17,0 to 19,0		8,0 to 10.5				0,10		1,00 to 3,00		—
X3CrNiCu18-9-4	4567-304-30-1	0,04		1,00		2,00		0,045		0,030		17,0 to 19,0		8,5 to 10,5 b		—		0,10		3,00 to 4,00		—
X3CrNiCu19-9-2	4560-304- 75-E	0,035		1,00		1,50 to 2,00		0,045		0,015		18,0 to 19,0		8,0 to 9,0		—		0,10		1,50 to 2,00		—
X5CrNi18-10	4301-304- 00-1	0,07		1,00		2,00		0,045		0,030		17,5 to 19,5		8,0 to 10,5		—		0,10		1,00		—
X6CrNiTi18-10	4541-321-00-1	0,08		1,00		2,00		0,045		0,030		17,0 to 19,0		9,0 to 12,0				一		1,00		Ti=5xC to 0,70
X2CrNi19-11	4306-304- 03-1	0,030		1,00		2,00		0,045		0,030		18,0 to 20,0		10,0 to 12,0		—		0,10		1,00		—
X6CrNi18-12	4303-305- 00-I	0,08		1,00		2,00		0,045		0,030		17,0 to 19,0-		10,5 to 13,0				0,10		—		——
X3NiCr18-16	4839-384- 00-1	0,04d		1,00		2,00		0,045		0,030		15,0 to 17,0		17,0 to 19,0		—		一		——
Austenitic steels with Mo
X2CrNiMo17-12-2	4404-316- 03-1	0,030		1,00		2,00		0,045		0,030		16,5 to 18,5		10,0 to 13,0		2,00 to 3,00		0,10		1,00
Elements not quoted in this table may not be intentionally added to the steel without the agreement of the purchaser except for finishing the heat.All appropriate precautions are to be taken to avoid the addition of such elements from scrap and other materials used in production that would impair mechanical properties and the suitability of the steel. Maximum values unless otherwise indicated A minimum content of8,0 %of Niis permitted,unless otherwise agreed at the time of enquiry and order. For this document,a range for Cr:16,5 to 19,0 is allowed. d For this document,C:0,08 is allowed. In order to improve the cold formability,a carbon content of max.0,04 %is recommended and may be agreed at the time of enquiry and order.

3.力学性能

表D.6-规定交货条件下的马丁不锈钢机械性能

Designation		Diameter		Delivery condition
Designation		Diameter		+A or +A+PE		+A+LC		+A+C+A		+A+C+A+LC
Steel name	ISO steel number	above mm	up to mm	Rm max. MPa	Z min. %	Rm max. MPa	Z min. %	Rm max. MPa	Z min. %	Rm max. MPa	Z min. %
X12Cr13	4006-410- 00-1	0,8	2							740	58
		2	5		—	——	——	600	60	660	58
		5	10	600	60	720	57	600	60	640	58
		10	25	600	60	700	57	600	60	640	58
		25	100	600	60	—	—	—	—	—